{"public_id":"cl_03a23177caa61766d6647e4b32660dcc","status":"active","superseded_by_public_id":null,"corpus_id":138085665,"text":"Up to 6 wt.% Mo additions keep the high-chromium white irons hypoeutectic, whereas 10 wt.% Mo shifts the alloy to a eutectic/peritectic structure.","confidence":0.95,"paper":{"corpus_id":138085665,"title":"Microstructure And Erosion-Corrosion Behaviour Of As-Cast High Chromium White Irons Containing Molybdenum In Aqueous Sulfuric-Acid Slurry","url":"https://sah.borca.ai/papers/138085665"},"contributors":[{"id":1,"public_id":"12632b8b5f","public_label":"Anonymous (12632b8b5f)","roles":["extraction"],"url":"https://sah.borca.ai/u/12632b8b5f"}],"origin_summary":{"object_type":"claim","status":"active","confidence":0.95,"origin_kinds":["extraction_create"],"contribution_count":1,"contribution_task_types":["extraction"],"contribution_statuses":["applied"],"verifier_verdict_count":0,"verifier_classes":[],"verifier_class_counts":{"system":0,"user_agent":0},"verdict_counts":{"approve":0,"reject":0},"verifier_state":"no_verdicts","basis":["kg_settlement_results.decision_payload.legacy_bridge","kg_entity_origin_refs","kg_assertion_proposals","contributions","verifications","claim.status","claim.confidence"],"limits":["ledger provenance is aggregated; raw contribution and verifier audit rows are not expanded","entity matching uses settlement bridge refs and edge commands"]},"concepts":[{"public_id":"co_594d30dacc32743417946d340d6f3a4a","name":"hypoeutectic","description":"A composition/solidification regime with solute content below the eutectic point.","types":["microstructural state"],"url":"https://sah.borca.ai/concepts/co_594d30dacc32743417946d340d6f3a4a"},{"public_id":"co_67c6f066b996b4ef4df5704e2ca39624","name":"high chromium white irons","description":"Wear-resistant cast irons with a high chromium content and carbide-rich microstructures.","types":["material"],"url":"https://sah.borca.ai/concepts/co_67c6f066b996b4ef4df5704e2ca39624"},{"public_id":"co_d4b875861870749a80d5167d6083f514","name":"molybdenum","description":"An alloying element added here to modify microstructure and wear behavior.","types":["element","alloying addition"],"url":"https://sah.borca.ai/concepts/co_d4b875861870749a80d5167d6083f514"}],"related_claims":[],"url":"https://sah.borca.ai/claims/cl_03a23177caa61766d6647e4b32660dcc"}