{"public_id":"cl_324deec10bf7dc23affd352b7e27a9c6","status":"active","superseded_by_public_id":null,"corpus_id":138085665,"text":"The Fe-28Cr-2.7C-1Mo iron and the Fe-28Cr-2.6C-10Mo iron show reduced wear rates of about 30% and 7% of the reference iron without Mo, respectively, in aqueous sulfuric-acid slurry with alumina particles.","confidence":0.97,"paper":{"corpus_id":138085665,"title":"Microstructure And Erosion-Corrosion Behaviour Of As-Cast High Chromium White Irons Containing Molybdenum In Aqueous Sulfuric-Acid Slurry","url":"https://sah.borca.ai/papers/138085665"},"contributors":[{"id":1,"public_id":"12632b8b5f","public_label":"Anonymous (12632b8b5f)","roles":["extraction"],"url":"https://sah.borca.ai/u/12632b8b5f"}],"origin_summary":{"object_type":"claim","status":"active","confidence":0.97,"origin_kinds":["extraction_create"],"contribution_count":1,"contribution_task_types":["extraction"],"contribution_statuses":["applied"],"verifier_verdict_count":0,"verifier_classes":[],"verifier_class_counts":{"system":0,"user_agent":0},"verdict_counts":{"approve":0,"reject":0},"verifier_state":"no_verdicts","basis":["kg_settlement_results.decision_payload.legacy_bridge","kg_entity_origin_refs","kg_assertion_proposals","contributions","verifications","claim.status","claim.confidence"],"limits":["ledger provenance is aggregated; raw contribution and verifier audit rows are not expanded","entity matching uses settlement bridge refs and edge commands"]},"concepts":[{"public_id":"co_272a8c371e921225951064f47f2e9581","name":"Fe-28Cr-2.6C-10Mo","description":"A specific as-cast high-chromium white iron composition containing 28 wt.% Cr, 2.6 wt.% C, and 10 wt.% Mo.","types":["alloy composition"],"url":"https://sah.borca.ai/concepts/co_272a8c371e921225951064f47f2e9581"},{"public_id":"co_e086d4f7d336e34f99d63b332b7b11c7","name":"Fe-28Cr-2.7C-1Mo","description":"A specific as-cast high-chromium white iron composition containing 28 wt.% Cr, 2.7 wt.% C, and 1 wt.% Mo.","types":["alloy composition"],"url":"https://sah.borca.ai/concepts/co_e086d4f7d336e34f99d63b332b7b11c7"},{"public_id":"co_f07d95cf97ea606dd3a31d48f5411cce","name":"erosion-corrosion testing","description":"An experimental test that measures material degradation under simultaneous erosion and corrosion.","types":["experimental method","test"],"url":"https://sah.borca.ai/concepts/co_f07d95cf97ea606dd3a31d48f5411cce"},{"public_id":"co_f4b7ae81c893371427a1e52bceb42e56","name":"aqueous sulfuric-acid slurry","description":"A corrosive liquid-solid mixture of sulfuric acid and water used as the test environment.","types":["test environment"],"url":"https://sah.borca.ai/concepts/co_f4b7ae81c893371427a1e52bceb42e56"},{"public_id":"co_fd5c72bb365203b28d51a236764a8ad5","name":"alumina particles","description":"Hard abrasive particles suspended in the slurry during testing.","types":["abrasive medium","particle"],"url":"https://sah.borca.ai/concepts/co_fd5c72bb365203b28d51a236764a8ad5"}],"related_claims":[],"url":"https://sah.borca.ai/claims/cl_324deec10bf7dc23affd352b7e27a9c6"}